The application of metal dental restorations in oral prosthetics has become very widespread and popular. Due to the complexity of the intraoral environment, it has been the focus of research to improve the mechanical and chemical properties, especially the corrosion resistance, to increase the durability of restorations under the premise of ensuring the good biocompatibility of the materials.Haoka et al. tested the electrochemical properties of niobium-containing magnetic attachments, and the results showed that compared with the traditional magnetic attachments, the magnetic attachments made of Pt-30.0mass%Fe-0.6mass%Nb alloys had better corrosion resistance.Lee et al. tested the electrochemical properties of titanium-niobium alloys. Lee et al. tested the structural properties of titanium-niobium alloys and showed that Ti-10Nb and Ti-27.5Nb alloys had the highest strength, while Ot' phase-dominated (17.5Nb, 20Nb) alloys and B-phase-dominated alloys (>30Nb) turėjo mažiausią tamprumo modulį. . Be to, visi titano ir niobio lydiniai, dalyvaujantys bandymuose, parodė puikų atsparumą korozijai.

Kikuchi ir kt. išbandytos liejamo titano-niobio lydinių, turinčių skirtingą savitąjį niobio tankį, mechanines savybes ir rezultatai parodė, kad titano lydinių, kurių sudėtyje yra 5 masės % niobio, kietumas žymiai padidėjo; titano lydinių, kurių sudėtyje yra 10 masės % niobio ir daugiau, išeiga ir tempiamasis stipris žymiai padidėjo, o pailgėjimas žymiai sumažėjo; titano lydiniai, kuriuose yra 30 masės % niobio, pasižymėjo geresnėmis abrazyvinėmis savybėmis, išlaikant didesnį kietumą, stiprumą ir elastingumo modulį. Hu Xin ir kt. atliktas tyrimas. taip pat patvirtino, kad didelio stiprumo, didelio tamprumo modulio titano-cirkonio-niobio-alavo lydinys yra metalinė medžiaga, turinti gerą biologinį saugumą burnos restauracijoms, tačiau dilimo mechanizmas keičiasi nuo abrazyvinio nusidėvėjimo iki klijų, didėjant paviršiaus apkrovai.